PA66 glass fiber is glass fiber reinforced nylon, the addition of glass fibers enhances the plastic strength, stiffness and provide heat distortion temperature. It can apply on different product production such as: industrial parts, Motor parts, Office Chair Base, and more.
PA66
33% glass fiber reinforced
Natural color, providing custom dyeing service
RoHS、REACH
25kg
High stiffness and strength, heat resistance and dimensional stability
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 1700 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 2600 |
Flexural Modulus | ASTM D790 | kg/cm2 | 80000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
14 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 245 |
Other | |||
Shrinkage | ASTM D955 | % | 0.2~0.4 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.38 |
Ash Content | ASTM D482 | % | 33 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |
PA66
50% glass fiber reinforced
Natural color, providing custom dyeing service
RoHS、REACH
25kg
More excellent high stiffness and strength, heat resistance and dimensional stability
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 2200 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 3400 |
Flexural Modulus | ASTM D790 | kg/cm2 | 130000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
17 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 255 |
Other | |||
Shrinkage | ASTM D955 | % | 0.2~0.4 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.55 |
Ash Content | ASTM D482 | % | 50 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |
PA66
15% glass fiber reinforced
Black
RoHS、REACH、GRS(Global Recycle Standard)
25kg
High stiffness, strength and thermal stability properties
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 900 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 1500 |
Flexural Modulus | ASTM D790 | kg/cm2 | 45000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
5 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
115 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 230 |
Other | |||
Shrinkage | ASTM D955 | % | 0.3~0.8 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.23 |
Ash Content | ASTM D482 | % | 15 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |
PA66
33% glass fiber reinforced
Black
RoHS、REACH、GRS(Global Recycle Standard)
25kg
High stiffness and strength, heat resistance and dimensional stability
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 1850 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 2900 |
Flexural Modulus | ASTM D790 | kg/cm2 | 95000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
14 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 245 |
Other | |||
Shrinkage | ASTM D955 | % | 0.2~0.4 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.38 |
Ash Content | ASTM D482 | % | 33 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |
PA66
33% glass fiber reinforced
Black
RoHS、REACH、GRS(Global Recycle Standard)
25kg
High stiffness and strength, heat resistance and dimensional stability
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 1350 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 2500 |
Flexural Modulus | ASTM D790 | kg/cm2 | 85000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
9 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 245 |
Other | |||
Shrinkage | ASTM D955 | % | 0.2~0.4 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.38 |
Ash Content | ASTM D482 | % | 33 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |
PA66
33% glass fiber reinforced
Black
RoHS、REACH、GRS(Global Recycle Standard)
25kg
High stiffness and strength, heat resistance and hydrolysis resistance
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 1800 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 2800 |
Flexural Modulus | ASTM D790 | kg/cm2 | 90000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
14 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 245 |
Other | |||
Shrinkage | ASTM D955 | % | 0.2~0.4 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.38 |
Ash Content | ASTM D482 | % | 33 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |
PA66
50% glass fiber reinforced
Black
RoHS、REACH
25kg
More excellent high stiffness and strength, heat resistance and dimensional stability
1. Materials Standard:
Test Items Property | Test Method | Unit | Vaule |
---|---|---|---|
Mechanical Properties | |||
Tensile Strength | ASTM D638 | Kg/cm2 | 2100 |
Elongation at Break | ASTM D638 | % | < 5 |
Flexural Strength | ASTM D790 | kg/cm2 | 3500 |
Flexural Modulus | ASTM D790 | kg/cm2 | 140000 |
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
16 |
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
Thermal | |||
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 255 |
Other | |||
Shrinkage | ASTM D955 | % | 0.2~0.4 |
Melt Index | ASTM D1238 | g/10min | - |
Specific Gravity | ASTM D792 | - | 1.55 |
Ash Content | ASTM D482 | % | 50 |
Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
Drying | Melt Temp | Inject Press. |
---|---|---|
80~100°C*4HR | 245~280°C | 20kg/cm2 |