HOME / Products / Ocean Plastic / Glass Fiber Reinforced Grade
Ocean Plastic

Ocean Plastic

Glass Fiber Reinforced Grade

Enhanced strength, stiffness and heat distortion temperature

A2000G15BK

Material Material：

PA6

Specification Specification：

15% Glass Fiber Reinforced

Color Color：

Black

Certification Certification：

RoHS、REACH、GRS、UL

Package Package：

25kg

Property Property：

Enhanced hardness, strength and heat resistance

A2000G15BK Add to Inquriy Cart Download

1. Materials Standard:

Test Items Property Test Method Unit Vaule
Mechanical Properties
Tensile Strength ASTM D638 Kg/cm2 1100
Elongation at Break ASTM D638 % < 5
Flexural Strength ASTM D790 kg/cm2 1500
Flexural Modulus ASTM D790 kg/cm2 50000
IZOD Impact, Notched 1/8" 23°C
IZOD Impact, Notched 1/8" -30°C 		ASTM D256 kg-cm/cm 6
Hardness Shore D
Hardness Rockwell R Scale 		ASTM D2240
ASTM D785 		-
115
Thermal
Heat Deflection Temperature
(18.6kg/cm2 ) 		ASTM D648 °C 180
Other
Shrinkage ASTM D955 % 0.2~0.6
Melt Index ASTM D1238 g/10min -
Specific Gravity ASTM D792 - 1.24
Ash Content ASTM D482 % 15
Equilibrium Moisture Content ASTM D570 % < 0.3
Flammability UL 94 1.6mm -

2. Molding Condition:

Drying Melt Temp Inject Press.
80~100°C*4HR 235~260°C 20kg/cm2

Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.

Applications

Electrical and Pneumatic Hand Tools - Hot Melt Glue Gun Housing
Industrial Parts & Components - Light Bulb Holder
Sporting equipment, Hand Tool, Bicycle brake parts, Home appliance parts, Motor housings, Hair dryer nozzle

A2000G33BK

Material Material：

PA6

Specification Specification：

33% Glass Fiber Reinforced

Color Color：

Black

Certification Certification：

RoHS、REACH、GRS、UL

Package Package：

25kg

Property Property：

Having excellent properties of high stiffness, strength and heat resistance

A2000G33BK Add to Inquriy Cart Download

1. Materials Standard:

Test Items Property Test Method Unit Vaule
Mechanical Properties
Tensile Strength ASTM D638 Kg/cm2 1500
Elongation at Break ASTM D638 % < 5
Flexural Strength ASTM D790 kg/cm2 2600
Flexural Modulus ASTM D790 kg/cm2 83500
IZOD Impact, Notched 1/8" 23°C
IZOD Impact, Notched 1/8" -30°C 		ASTM D256 kg-cm/cm 12
Hardness Shore D
Hardness Rockwell R Scale 		ASTM D2240
ASTM D785 		-
120
Thermal
Heat Deflection Temperature
(18.6kg/cm2 ) 		ASTM D648 °C 200
Other
Shrinkage ASTM D955 % 0.2~0.6
Melt Index ASTM D1238 g/10min -
Specific Gravity ASTM D792 - 1.38
Ash Content ASTM D482 % 33
Equilibrium Moisture Content ASTM D570 % < 0.3
Flammability UL 94 1.6mm -

2. Molding Condition:

Drying Melt Temp Inject Press.
80~100°C*4HR 235~260°C 20kg/cm2

Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.

Applications

Electrical and Pneumatic Hand Tools - Hot Melt Glue Gun Housing
Office Chairs - Office Chair Armrest
Sports equipment, Hand tools, Bicycle brake parts, Office desk & chair, Home appliance parts, Motor housings, Hair dryer nozzle

A2000G45BK

Material Material：

PA6

Specification Specification：

45% Glass Fiber Reinforced

Color Color：

Black

Certification Certification：

RoHS、REACH、GRS、UL

Package Package：

25kg

Property Property：

It has the characteristics of high rigidity, high strength and heat resistance

A2000G45BK Add to Inquriy Cart Download

1. Materials Standard:

Test Items Property Test Method Unit Vaule
Mechanical Properties
Tensile Strength ASTM D638 Kg/cm2 1950
Elongation at Break ASTM D638 % < 5
Flexural Strength ASTM D790 kg/cm2 3250
Flexural Modulus ASTM D790 kg/cm2 115000
IZOD Impact, Notched 1/8" 23°C
IZOD Impact, Notched 1/8" -30°C 		ASTM D256 kg-cm/cm 16
Hardness Shore D
Hardness Rockwell R Scale 		ASTM D2240
ASTM D785 		-
120
Thermal
Heat Deflection Temperature
(18.6kg/cm2 ) 		ASTM D648 °C 210
Other
Shrinkage ASTM D955 % 0.1~0.4
Melt Index ASTM D1238 g/10min -
Specific Gravity ASTM D792 - 1.50
Ash Content ASTM D482 % 45
Equilibrium Moisture Content ASTM D570 % < 0.3
Flammability UL 94 1.6mm -

2. Molding Condition:

Drying Melt Temp Inject Press.
80~100°C*4HR 235~260°C 20kg/cm2

Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.

Applications

Baby Strollers - Buckle Axle
Sports Equipment, Pneumatic Tool Housing, Hand tool, Bicycle brake parts, Fishing tackle reels, Scroll doors, Office desks and chairs, Home appliance parts, Motor housings, Hair dryer nozzle

A2000G50BK

Material Material：

PA6

Specification Specification：

50% Glass Fiber Reinforced

Color Color：

Black

Certification Certification：

RoHS、REACH、GRS、UL

Package Package：

25kg

Property Property：

More excellent properties such as high rigidity and strength, heat resistance and dimensional stability

A2000G50BK Add to Inquriy Cart Download

1. Materials Standard:

Test Items Property Test Method Unit Vaule
Mechanical Properties
Tensile Strength ASTM D638 Kg/cm2 2100
Elongation at Break ASTM D638 % < 5
Flexural Strength ASTM D790 kg/cm2 3300
Flexural Modulus ASTM D790 kg/cm2 117000
IZOD Impact, Notched 1/8" 23°C
IZOD Impact, Notched 1/8" -30°C 		ASTM D256 kg-cm/cm 18
-
Hardness Shore D
Hardness Rockwell R Scale 		ASTM D2240
ASTM D785 		- -
120
Thermal
Heat Deflection Temperature
(18.6kg/cm2 ) 		ASTM D648 °C 210
Other
Shrinkage ASTM D955 % 0.1~0.4
Melt Index ASTM D1238 g/10min -
Specific Gravity ASTM D792 - 1.55
Ash Content ASTM D482 % 50
Equilibrium Moisture Content ASTM D570 % < 0.3
Flammability UL 94 1.6mm -

2. Molding Condition:

Drying Melt Temp Inject Press.
80~100°C*4HR 235~260°C 20kg/cm2

Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.

Applications

Baby Strollers - Buckle Axle
Sports Equipment, Pneumatic Tool Housing, Hand tool, Bicycle brake parts, Fishing tackle reels, Scroll doors, Office desks and chairs, Home appliance parts, Motor housings, Hair dryer nozzle