PA/ABS Composite Material
Ultra Impact Modified Grade
Increase the toughness of PA/ABS at low temperatures.
F1000TNC
Material：
PA/ABS
Specification：
Low Temperature Impact Resistance
Color：
Natural color, providing custom dyeing service
Certification：
RoHS、REACH
Package：
25kg
Property：
Excellent ultra high toughness, low temperature impact resistance and surface improved
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 450 |
| Elongation at Break | ASTM D638 | % | > 70 |
| Flexural Strength | ASTM D790 | kg/cm2 | 750 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 18500 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
70 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
76 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | - |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | - |
| Specific Gravity | ASTM D792 | - | 1.06 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 245~280°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.
Applications
Sports equipment, Buckle