PA66
Ultra Impact Modified Grade
Increase the toughness of nylon at low temperatures.
Our ultra impact modified PA66 is a grade of PA66 that has been specially formulated to improve its impact resistance, especially at low temperatures. This makes it ideal for applications where parts need to be able to withstand impact and stress in cold environments.
It can also be used to make sporting goods that need to be able to withstand the cold winters of northern climates.
B2000TSDA3
Material：
PA66
Specification：
Low Temperature Impact Resistance
Color：
Natural color, providing custom dyeing service
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent ultra high toughness, low temperature impact resistance and surface improved
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 450 |
| Elongation at Break | ASTM D638 | % | > 70 |
| Flexural Strength | ASTM D790 | kg/cm2 | 700 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 18000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 85 20 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
80 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 5 |
| Specific Gravity | ASTM D792 | - | 1.07 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 245~280°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.
B6000TBKA3
Material：
PA66
Specification：
Low Temperature Impact Resistance
Color：
Black
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent ultra high toughness, low temperature impact resistance and surface improved
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 450 |
| Elongation at Break | ASTM D638 | % | > 70 |
| Flexural Strength | ASTM D790 | kg/cm2 | 800 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 17500 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 80 16 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
72 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 10 |
| Specific Gravity | ASTM D792 | - | 1.07 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 245~280°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.